Anticora EZC 500
Epoxy Zinc Chrome Primer
Product Description
Anticora EZC 500 is a two-component epoxy polyamide
anticorrosive high performance primer containing zinc chrome as rust inhibitive
pigment. It cures to a tough and highly rust preventive coat.
Features and Benefits
Easy to apply
and can be applied via airless spray, conventional spray, brush or roller.
Ideal for use
as a field primer on interior and exterior steel as part of a system to be
topcoated with chlorinated rubber, epoxy and polyurethane topcoats.
A rust
inhibitive primer over iron and steel and protects steel from atmospheric
corrosion.
Provides much
higher degree of protection than conventional primers in severe corrosive
conditions.
Excellent
resistance to acids, alkalis, water, salts, oils, petroleum solvents.
Has very low
water and water vapour permeability.
Has excellent
adhesion, toughness, abrasion resistance and overall chemical and solvent
resistance.
While inferior
surface preparation can never be recommended, Anticora EZC 500 can
tolerate, though with shorter life, power tool and hand cleaned steel
surfaces.
Ideal for high humidity, moisture, marine atmospheres, heavy rains, high temperatures, damp conditions, very low dusty and fungus prone conditions.
Durable and economical.
Recommended uses
Blasted Steel structures |
Off-shore structures |
Petroleum Refineries |
Sewage Equipment |
Railway Wagons & Coaches |
Pulp & Paper Mills |
Water Treatment Plants |
Chemical Plants |
Pipelines |
Fertilizer Plants |
Power Plants |
Marine & Shore Installations |
Surface Preparation
Steel
- The surface should be blast cleaned to SSPC-SP
10-63T or NACE No. 2 i.e. loose rust and scales, dirt, grease, oil,
paint, wax, weak oxide films and other contaminants should be removed. Blast
cleaning to SSPC-SP 5-63 or NACE No. 1
is recommended where heavy corrosive conditions exist or coating is required to
be immersed. That means a surface with a grey metallic colour, slightly
roughened to form a suitable anchor pattern for coatings. This surface is free
of all oil, grease, dirt, mill scale, rust, corrosion products, oxides, paint
and other foreign matter. In absence of blast cleaning, prepare the metal
surface by wire brushing, sanding, grinding, scrapping or chipping with hand or
power tools. Remove all the contaminants. Apply one coat of Anticora
EZC 500. It can be overcoated with Durapoxy
200 Epoxy Enamel, Anuthane
Enamel Polyurethane or Monocoat
Enamel Polyurethane, Anuchlor
555 LB Chlorinated Rubber Enamel.
Non-ferrous Metals - Remove dirt, dust, oil, old paint etc. Degrease the surface with degreasing solvents like xylene or tri-chloroethylene. Apply one coat of Anuprime - 291 Wash Primer for obtaining maximum adhesion. Apply one or two coats of Anticora EZC 500.
TECHNICAL DATA
Name/Description |
Anticora EZC 500 |
Type |
Two pack cold cured |
Composition |
Epoxy / Zinc Chrome |
Colour |
Yellow |
Finish |
Smooth and Matt |
Volume Solids (mixed) |
44± 3% |
Mixing Ratio |
Base : Hardener 3 : 1 by volume |
Pot Life @ 30° C |
6 to 8 hours |
Dry film thickness per coat |
25 to 30 microns |
Coverage-(theoretical-no loss) |
17.6 to 14.6 m² /litre |
Serviceability @ 30°
C Dry to touch Hard Dry Recoat Full Cure |
1 hour Overnight 24 hours 7 days |
Induction (Sweat-in-time) @ 30°C |
30 minutes |
Dry heat resistance |
120° C |
Relative Humidity |
90% |
Application Temperature -minimum -maximum |
10° C 35° C |
Solvent/Thinner |
Anusol - ETP Thinner |
Flash Point |
25° C |
Packing |
4 & 20 litres |
Shelf Life |
6 months |
Precaution |
Flammable. Keep away from heat and open flame. Maintain good ventilation and avoid breathing vapours. |
Notes:
Brushes and spray equipments should be cleaned with Anusol - ETP Epoxy Thinner.
The contents should be stirred thoroughly prior to use.
After mixing Base and Hardener in recommended proportions, allow for 30
minutes induction period or sweat-in-time (maturing) before application.
When overcoating the weathered Anticora EZC 500, ensure that the coating is free from all contamination like oil, dust, grease, grease stains.
This coating should always be thinned with Anusol - ETP Epoxy Thinner. The use of alternative thinners can severely inhibit the curing mechanism of the coating.
Disclaimer:
Information provided herein is based upon tests believed to be reliable. It does not guarantee the results to be obtained. Nor does it make any express and implied warranty or merchantability, or fitness for a particular purpose concerning the effects or results of such case. It does not release you from the obligation to test the products supplied by us as to their suitability for the intended uses. The application, surface preparation and use of the products are beyond our control and, therefore, entirely your own responsibility.